聚酰胺66

Ascend Performance Materials Operations LLC

Technical Data

 

产品说明

 

Vydyne 20NSP is a general-purpose, highly nucleated, lubricated PA66 resin available in natural color. It is designed to crystallize rapidly in order to reduce cycle times and increase productivity through faster part set-up. The higher crystalline structure will increase tensile modulus and strength, reduce elongation and may slightly lower mold shrinkage when compared to standard general-purpose non nucleated PA66. The rapid crystallization of Vydyne 20NSP resin may allow part ejection at a higher temperature compared to general-purpose PA66. Critical factors unique to each application such as mold design, part design, tolerances and other factors will dictate ultimate cycle time benefits. It is recommended to check critical part dimensions against specifications before adopting shorter molding cycles. Vydyne 20NSP resin has an external lubricant for improved machine feed and an internal lubricant for improved mold release.

 

Typical Applications/End Uses:

End uses for Vydyne 20NSP include terminal blocks, bearings, control cams, electrical connectors, housings, cable ties, fasteners, switch components and industrial parts that require chemical resistance, stiffness, wear resistance and rigidity.

 

总体

 

材料状态 • 已商用：当前有效

资料 1 •  Technical Datasheet

UL 黄卡 2 •  E70062-249058

搜索 UL 黄卡 •  Ascend Performance Materials Operations LLC

•  Vydyne®

供货地区 • 北美洲 • 欧洲 • 亚太地区

添加剂 • 成核剂 • 润滑剂

• 成核的 • 快的成型周期 • 脱模性能良好

特性 • 刚性，高 • 润滑

• 刚性，良好 • 通用

• 工业应用 • 通用 • 轴承

用途 • 紧固件 • 凸轮

• 连接器 • 外壳

机构评级 • ASTM D 4066 PA0131 • ASTM D 6779 PA0131 • FED L-P-410A

RoHS 合规性 • RoHS 合规

UL文件号 • E70062

外观 • 自然色

形式 • 粒子

加工方法 • 注射成型

多点数据 • Isothermal Stress vs. Strain (ISO 11403-1)

物理性能 干燥 调节后的 单位制 测试方法

密度 1.14 -- g/cm³ ISO 1183

收缩率 ISO 294-4

垂直流动方向 : 23°C, 2.00 mm 1.6 -- %

流动方向 : 23°C, 2.00 mm 1.4 -- %

吸水率 ISO 62

23°C, 24 hr 1.2 -- %

平衡, 23°C, 50% RH 2.4 -- %

机械性能 干燥 调节后的 单位制 测试方法

拉伸模量 (23°C) 3800 2500 MPa ISO 527-2

拉伸应力 ISO 527-2

屈服, 23°C 95.0 60.0 MPa

断裂, 23°C 75.0 50.0 MPa

拉伸应变 (屈服, 23°C) 5.0 15 % ISO 527-2

标称拉伸断裂应变 (23°C) 13 20 % ISO 527-2

弯曲模量 (23°C) 3200 1300 MPa ISO 178

弯曲强度 (23°C) 100 35.0 MPa ISO 178

泊松比 0.40 -- ISO 527-2

 

 

Vydyne® 20NSP

聚酰胺66

Ascend Performance Materials Operations LLC

冲击性能 干燥 调节后的 单位制 测试方法

简支梁缺口冲击强度 ISO 179/1eA

-30°C 5.0 5.0 kJ/m²

23°C 6.0 15 kJ/m²

简支梁无缺口冲击强度 ISO 179/1eU

-30°C 无断裂 无断裂

23°C 无断裂 无断裂

悬壁梁缺口冲击强度 ISO 180

-30°C 5.0 5.0 kJ/m²

23°C 6.0 15 kJ/m²

热性能 干燥 调节后的 单位制 测试方法

热变形温度

0.45 MPa, 未退火 230 -- °C ISO 75-2/B

1.8 MPa, 未退火 90.0 -- °C ISO 75-2/A

熔融温度 260 -- °C ISO 11357-3

线形热膨胀系数 ISO 11359-2

流动 : 23 到 55°C, 2.00 mm 1.0E-4 -- cm/cm/°C

横向 : 23 到 55°C, 2.00 mm 1.0E-4 -- cm/cm/°C

RTI Elec UL 746

0.400 mm 130 -- °C

0.710 mm 130 -- °C

1.50 mm 130 -- °C

3.00 mm 130 -- °C

RTI Imp UL 746

0.400 mm 75.0 -- °C

0.710 mm 75.0 -- °C

1.50 mm 75.0 -- °C

3.00 mm 75.0 -- °C

RTI UL 746

0.400 mm 75.0 -- °C

0.710 mm 85.0 -- °C

1.50 mm 85.0 -- °C

3.00 mm 85.0 -- °C

电气性能 干燥 调节后的 单位制 测试方法

体积电阻率 (0.750 mm) 1.0E+10 -- ohm•cm IEC 60093

介电强度 (1.00 mm) 26 -- kV/mm IEC 60243

耐电弧性 (3.00 mm) PLC 5 -- ASTM D495

漏电起痕指数 (3.00 mm) 600 -- V IEC 60112

高电弧燃烧指数(HAI) UL 746

0.710 mm PLC 0 --

1.50 mm PLC 0 --

3.00 mm PLC 0 --

高电压电弧起痕速率 (HVTR) PLC 0 -- UL 746

热丝引燃 (HWI) UL 746

0.710 mm PLC 4 --

1.50 mm PLC 3 --

3.00 mm PLC 3 --

可燃性 干燥 调节后的 单位制 测试方法

UL 阻燃等级 UL 94

0.400 mm V-2 --

0.710 mm V-2 --

1.50 mm V-2 --

3.00 mm V-2 --

 

Vydyne® 20NSP

聚酰胺66

Ascend Performance Materials Operations LLC

可燃性 干燥 调节后的 单位制 测试方法

灼热丝易燃指数 IEC 60695-2-12

0.710 mm 800 -- °C

1.50 mm 800 -- °C

3.00 mm 930 -- °C

热灯丝点火温度 IEC 60695-2-13

0.710 mm 700 -- °C

1.50 mm 700 -- °C

3.00 mm 700 -- °C

极限氧指数 26 -- % ISO 4589-2

注射 干燥单位制

干燥温度 < 70.0°C

干燥时间 1.0 到 3.0hr

建议的最大回制料比例 50%

料筒后部温度 260 到 280°C

料筒中部温度 270 到 285°C

料筒前部温度 280 到 290°C

射嘴温度 280 到 300°C

加工（熔体）温度 285 到 300°C

模具温度 65.0 到 95.0°C

 

 

 

 

 